XR 5

XR-5® 8130 Reinforced

Standard

Metric

Base Fabric Type
ASTM D3776

Polyester

Base Fabric Weight (nominal)
ASTM D3776

6.5 oz/yd²

220 g/m²

Thickness
ASTM D751

30.0 mils min.

0.76 mm min.

Weight
ASTM D751

30.0 ± 2 oz/yd²

1017 ± 70 g/m²

Tear Strength
ASTM D4533, Trapezoid Tear

35/35 lb_f min.

155/155 N min.

Breaking Yield Strength
ASTM D751, Grab Tensile

550/550 lb_f min.

2447/2447 N min.

Low Temperature
ASTM D2136, 4 hr - 1/8" mandrel

Pass @ -30 º F

Pass @ -35 º C

Dimensional Stability
ASTM D1204, 212º F - 1 hr

1.5% max.
each direction

Adhesion - Heat Sealed Seam
ASTM D751, Dielectric Weld

35 lb_f/2 in min.

15 daN/5 cm min.

Dead Load - Seam Shear Strength
ASTM D751

2 in seam, 4 hr, 1 in strip
210 lb_f @ 70º F
105 lb_f @ 160º F

5 cm seam, 4 hr, 2.5 cm strip
934 N @ 21º C
467 N @ 70º C

Bursting Strength
ASTM D751 Ball Tip

650 lb_f min.
800 lb_f typical

2892 N min.
3560 N typical

Hydrostatic Resistance
ASTM D751, Method A

800 psi min.

5.51 MPa min.

Blocking Resistance
ASTM D751 (180º F/82º C)

# 2 Rating max.

Adhesion - Ply
ASTM D413

15 lb_f/in min.
or Film Tearing Bond

13 daN/5 cm min.
or Film Tearing Bond

Bonded Seam Strength
ASTM D751 as modified by NSF 54

550 lb_f min.

2447 N min.

Abrasion Resistance
ASTM D3389 (H-18 Wheel, 1000 g load)

2000 cycles (min.) before fabric exposure
50 mg/100 cycles max weight loss

Weathering Resistance
ASTM G23 (Carbon-Arc)

8,000 hrs (min.) - No appreciable changes
or stiffening or cracking of coating

Water Absorption
ASTM D471, Section 12, 7 days

0.025 kg/m² max. @ 70º F/21º C
0.14 kg/m² max. @ 212º F/100º C

Wicking
Shelter-Rite^® Procedure

1/8 in max.

0.3 cm max.

Puncture Resistance
ASTM D4833

250 lb_f min.

1112 N min.

Coefficient of Thermal Expansion/Contraction
ASTM D696

8 x 10^-6 in/in/ºF max.

1.4 x 10^-5 cm/cm/ºC max.

We believe this information is the best currently available on the subject. We offer it as a suggestion in any appropriate experimentation you may care to undertake. It is subject to revision as additional knowledge and experience are gained. We make no guarantee of results and assume no obligation or liability whatsoever in connection with this information. In case of conflict between standard and metric specifications, standard shall apply.